HIGH FIRE-RESISTANT SILICONE SEALANT

FIRE SEALING SILICONE

FIRE SEALING SILICONE is a highly fire-resistant silicone sealant (class B-s1, d0), ideal for sealing linear joints in fire rated walls and doors in situations subject to fire regulations.

FIRE SEALING SILICONE, the silicone sealant with high fire resistance B-s1, d0

FIRE SEALING SILICONE is a tested protection silicone sealant, designed to offer maximum protection against the passage of flames, smoke or gases.

Ideal for sealing linear joints in fire rated walls and doors, in situations subject to fire regulations. It is classified, according to EN 15651-1, for indoor and outdoor non-structural uses, it can also be used on façades and in areas with cold climates. High adhesion and high UV resistance.

Documents

Technical data sheets
Declaration of performance (DOP) Download
Test Report
Fire test report

FIRE SEALING SILICONE

CODE content
[ml]
contenuto
[US fl oz]
colour version pcs.
FIRESILGRE310 310 10.48 GREY PLASTIC CARTRIDGE 24

Technical Data
EN 15651-1
EN 13501-1 B-s1,d0
EN 13501-5 EI240

Property Standard Tested Values USC Conversion
Composition - silicone -
Classification (1) EN 15651-1 F-EXT/INT-CC -
Density ISO 1183-1 1,482 g/mL 237.65 oz/gal
Yield for 10x10 mm joint - 3,1 m 10.17 ft
Surface cross-linking time 23 °C (2) - 80 minutes -
Hardening speed 20 °C / 50 %RH - ca. 2 mm/24h -
Shore A hardness DIN 53505 ca. 30 -
Elongation at failure DIN 53504 460 % -
Tensile strength DIN 53504 0,72 N/mm² 104 lbf/in²
Compressive modulus 100% DIN 53504 0,38 N/mm² 55 lbf/in²
Reaction to fire EN 13501-1 class B-s1,d0 -
Fire resistance (3) EN 13501-2 EI240 -
Acid resistance - excellent -
Bases resistance - excellent -
VOC content - 4.3 % - 64 g/L -
French VOC classification ISO 16000 A+ -
Emicode procedura di prova GEV EC1 -
Storage temperature (4) - 5 / 35 °C 41 / 95 °F
1.
2. The data expressed may vary depending on the thickness of the product applied and the specific installation conditions: temperature, humidity, ventilation, absorbency of the substrate.
3. Valid value for tested configurations