BREATHABLE SELF-ADHESIVE MEMBRANE

TRASPIR ADHESIVE 260

TRASPIR ADHESIVE 260 is the self-adhesive membrane that ensures strong adhesion even on the roughest substrates.

The special patented adhesive allows it to retain its breathable properties while still ensuring a secure seal. It features an Sd value of just 0.22 m and a very high capacity to speed up installation.

Videos

TRASPIR ADHESIVE 260 self-adhesive membrane: more practical installation, faster work.

The adhesive surface prevents the formation of airflow behind the membrane in case of accidental breakage or failure to seal.
Thanks to the patented glue, it remains perfectly breathable even when fully bonded: the fully self-adhesive surface of the membrane allows fast and safe installation without compromising performance.

It is ideal for pre-processing in the factory and also offers protection for CLT elements during transport and construction.

Documents

Technical data sheets
Declaration of performance (DOP) Download
File BIM.rfa
Recommendations for installation
TEST REPORT USA-CA

TRASPIR ADHESIVE 260

CODE description tape H
[m]
L
[m]
A
[m²]
H
[ft]
L
[ft]
A
[sft]
pcs./pallet
TA260 TRASPIR ADHESIVE 260 - 1.45 50 72.5 4' 9 1/8'' 164 780 16
TAS260 TRASPIR ADHESIVE 260 STRIPE - 0.36 50 18 1' 2 1/8'' 164 194 30

Technical Data
@300Pa ASTM E331 PASS A S TM
ASTM E2178 PASS A S TM
ASTM E96 100 US PERM A S TM
CAN/ULC-S741 PASS
national-classifications AT Önorm B4119 UD Typ I US
national-classifications CH SIA 232 UD (g)
national-classifications DE ZVDH USB-A UDB-A
national-classifications FR DTU 31.2 E1 Sd1 TR2 E600 Jf C1
national-classifications IT UNI 11470 A/R3
national-classifications AUS AS/NZS 4200.1 Class 4
national-classifications USA IRC Vp
AS 1530.2 Index 1
ASTM E84 | class 1 | class A

Property Standard Tested Values USC Conversion
Mass per unit area EN 1849-2 260 g/m² 0.85 oz/ft²
Thickness EN 1849-2 ca. 0,6 mm ca. 24 mil
Water vapour transmission (Sd) EN 1931 0,18 m 19.425 US perm
Water vapour transmission (dry cup) ASTM E96/ E96M 16.5 US perm -
Water vapour transmission (dry cup) ASTM E96/ E96M 885 ng/(s·m²·Pa) -
Tensile strength MD/CD EN 12311-1 315 / 250 N/50mm 36 / 29 lbf/in
Elongation MD/CD EN 12311-1 61 / 66 % -
Resistance to nail tearing MD/CD EN 12310-1 255 / 260 N 57 / 58 lbf
Watertightness EN 1928 class W1 -
Resistance to temperature - -30 / 80 °C -22 / 176 °F
Reaction to fire EN 13501-1 class E -
Resistance to penetration of air EN 12114 < 0,02 m³/(m²·h·50Pa) < 0.001 cfm/ft² at 50Pa
Thermal conductivity (λ) - 0,3 W/(m·K) 0.17 BTU/(h·ft·°F)
Specific heat - 1800 J/(kg·K) -
Density - 435 kg/m³ -
Water vapour resistance factor (μ) - ca. 300 -
Joint strength EN 12317-2 132 / N/50mm 15.074789 / lb/in
UV stability - 336h (3 months) -
Watertightness after artificial ageing EN 1297 / EN 1928 class W1 -
After artificial ageing - Tensile strength MD/CD EN 1297 / EN 12311-1 295 / 225 N/50mm 34 / 26 lb/in
After artificial ageing - elongation EN 1297 / EN 12311-1 45 / 47 % -
Solvents - no -
Application temperature - -5 / 35 °C 23 / 95 °F
Storage temperature - 5 / 30 °C 41 / 86 °F
Adhesion strength on OSB at 180° after 10 minutes EN ISO 29862 3,5 N/10mm 2 lbf/in
Adhesion strength on OSB at 90° after 10 minutes EN ISO 29862 2 N/10mm 1.1 lbf/in
Shear adhesion strength of the overlap after 24 hours EN 12317-2 16 N/50mm 1.8 lbf/in
Adhesion strength (average) of the overlap after 24 hours EN 12316-2 145 N/50mm 16.6 lbf/in
Total heat release rate ASTM E1354 8,21 MJ/m2 -
Flame spread index (FSI) ASTM E84 0 -
Smoke developed index (SDI) ASTM E84 15 -
Surface burning characteristics ASTM E84 class 1 or class A -
Airtightness (before and after ageing) CAN/ULC-S741 compliant -
Flammability index (1) AS 1530.2 < 5 -
1.

Specifications

TRASPIR ADHESIVE 260

Supply and installation of self-adhesive breathable membrane, like TRASPIR ADHESIVE 260.

Composition

From top layer to bottom layer:

non-woven PP fabric;

PP breathable film;

non-woven PP fabric;

breathable, durable and solvent-free glue;

removable plastic film.

Properties

Mass per unit area [g/m²]: 260

Thickness [mm]: approx. 0.6

Water vapour transmission (Sd) [m]: 0,18

Tensile strength MD/CD [N/50 mm]: 315/250

Elongation MD/CD [%]: 61/66

Resistance to nail tearing MD/CD [N]: 255/260

Watertightness: class W1 (EN 1928)

Reaction to fire: class E (EN 13501-1)

Resistance to temperature [°C]: - 30/80

UV stability: 336h (3 months)

Storage temperature [°C]: 5/30

Application temperature [°C]:- 5/35

Solvents: no

Standards and certifications

CE marked in accordance with EN 13859-½

AUS 4200.1 Class 4

ASTM E84 Class 1 – Class A

Description

The membrane can be used both as temporary protection during construction and transport phases, and as a long-term functional layer in building components (walls and floors).

The application surface must be dry, free of dust and grease, and not be anti-adhesive. Surface elements must be removed so that the membrane is not damaged during application.

Recommended use: direct UV protection is guaranteed. Installation is therefore permitted on both the internal and external sides of the building envelope.

Thanks to the new generation glue, the membrane ensures good adhesion even on rough OSB.

Installation:
Unroll the membrane over the surface to be protected, progressively remove the release film from the adhesive, and press the membrane firmly to ensure proper adhesion.

Ensure that the overlap between the membranes is at least 15 cm to achieve an optimal seal.

To ensure correct and professional installation, the use of a nail sealing point is required.

Further details on installation are available in the specific instructions provided by the supplier.

Composition

TOP LAYER non-woven PP fabric
middle layer PP breathable film
BOTTOM LAYER non-woven PP fabric
Adhesive layer acrylate dispersion without solvents
RELEASE LINER removable plastic film