New
TRASPIR EVO UV ADHESIVE
SELF-ADHESIVE BREATHABLE MONOLITHIC MEMBRANE RESISTANT TO UV RAYS
It consists of a special polymer compound and has an adhesive film that adheres perfectly to any substrate structure.
The monolithic structure provides excellent weather and chemical resistance, guaranteeing 10 weeks of protection if only the elements are covered.
It has fire reaction B-s1,d0 and flame retardant capacity according to EN 13501-1.
The low flame spread and the impossibility of forming flammable particles guarantees the safety of the building and people
TRASPIR EVO UV ADHESIVE
| CODE | description | g/m² | H
[m]
|
L
[m]
|
A
[m²]
|
H
[ft]
|
L
[ft]
|
A
[sft]
|
pcs./pallet |
|---|---|---|---|---|---|---|---|---|---|
| TUVA250 | TRASPIR EVO UV ADHESIVE 250 | 250 | 1.45 | 50 | 72.5 | 4' 9 1/8'' | 164 | 780 | - |
Technical Data
| Property | Standard | Tested Values | USC Conversion |
|---|---|---|---|
| Mass per unit area | EN 1849-2 | 250 g/m² | 0.82 oz/ft² |
| Thickness | EN 1849-2 | 0,7 mm | 28 mil |
| Water vapour transmission (Sd) | EN 1931 | 0,19 m | 18.403 US perm |
| Tensile strength MD/CD | EN 12311-1 | 270 / 225 N/50mm | 31 / 26 lbf/in |
| Elongation MD/CD | EN 12311-1 | 50 / 70 % | - |
| Resistance to nail tearing MD/CD | EN 12310-1 | 180 / 220 N | 40 / 49 lbf |
| Watertightness | EN 1928 | class W1 | - |
| Resistance to temperature | - | -30 / 120 °C | -22 / 248 °F |
| Reaction to fire | EN 13501-1 | class B-s1,d0 | - |
| Resistance to penetration of air | EN 12114 | 0,02 m³/(m²·h·50Pa) | 0.001 cfm/ft² at 50Pa |
| Thermal conductivity (λ) | - | 0,3 W/(m·K) | 0.17 BTU/(h·ft·°F) |
| Specific heat | - | 1800 J/(kg·K) | - |
| Density | - | 415 kg/m³ | - |
| Water vapour resistance factor (μ) | - | 475 | - |
| UV resistance without final coating | EN 13859-2 | 5000h (>12 mesi) | - |
| Weathering without final cladding | - | 10 weeks | - |
| Watertightness after artificial ageing | EN 1297 / EN 1928 | class W1 | - |
| After artificial ageing - Tensile strength MD/CD | EN 1297 / EN 12311-1 | 180 / 145 N/50mm | 21 / 17 lb/in |
| After artificial ageing - elongation | EN 1297 / EN 12311-1 | 38 / 31 % | - |
| Solvents | - | no | - |
| Watertightness at 120°C after artificial ageing | EN 1297 / EN 1928 | class W1 | - |
| Storage temperature | - | 5 / 35 °C | 41 / 95 °F |
| Application temperature | - | 5 / 25 °C | 41 / 77 °F |
| Flammability index (1 ) | AS 1530.2 | < 5 | - |
1.
Composition
| TOP LAYER | non-woven PP fabric |
|---|---|
| middle layer | breathable monolithic PU film |
| BOTTOM LAYER | non-woven PP fabric |
| GLUE | acrylic dispersion without solvents |
| RELEASE LINER | removable plastic film |
Specifications
TRASPIR EVO UV ADHESIVE
Supply and installation of UV-resistant monolithic breathable self-adhesive membrane, Type TRASPIR EVO UV ADHESIVE.
Composition
From top layer to bottom layer:
highly UV ray-stabilised PP non-woven fabric;
breathable monolithic PU film;
non-woven PP fabric;
acrylate dispersion without solvents;
precut removable plastic film.
Properties
Mass per unit area [g/m²]: 250
Thickness [mm]: approx. 0,7
Water vapour transmission (Sd)[m]: 0,19
Tensile strength MD/CD [N/50 mm]: 270/225
Elongation MD/CD [%]: 50/70
Resistance to nail tearing MD/CD [N]: 180/220
Watertightness: W1 (EN 1928)
Resistance to temperature [°C]: -30/+120
Reaction to fire: B-s1, d0 (EN 13501-1)
Storage temperature [°C]: +5/+35
Application temperature [°C]:+5/+25
Standards and certifications
CE marked in accordance with EN 13859-1/2
AUS 4200.1 Class 4
Description
The application surface must be dry, free of dust and grease, and not be anti-adhesive. Surface elements must be removed so that the membrane is not damaged during application.
Recommended use: direct UV protection is guaranteed. Installation is therefore permitted on both the internal and external sides of the building envelope.
Installation: Unroll the membrane, progressively remove the release film from the adhesive, and press the membrane firmly to ensure proper adhesion.
Ensure that the overlap between the membranes is at least 15 cm to achieve an optimal seal.
If installed on walls, the membrane must be laid horizontally, starting from the base of the wall and progressing upwards to the top.
To ensure correct and professional installation, the use of a nail sealing point is required.
Further details regarding installation can be found in the specific instructions provided by the supplier.