TRASPIR FELT EVO UV 210
MONOLITHIC BREATHABLE MEMBRANE RESISTANT TO UV RAYS
TRASPIR FELT EVO UV 210 is the monolithic breathable membrane with exceptional UV resistance. It is the ideal solution for creating discontinuous coating of ventilated façades with grouting up to 30 mm wide.
Description
TRASPIR FELT EVO UV 210: waterproofing and UV stability in one solution.
It consists of a monolithic breathable PU layer on a polyester reinforcement and is designed for application on the external side of walls.
Documents
-
Technical data sheets
-
Recommendations for installation
Technical Data
| Property | Standard | Tested Values | USC Conversion |
|---|---|---|---|
| Mass per unit area | EN 1849-2 | 210 g/m² | 0.69 oz/ft² |
| Thickness | EN 1849-2 | 1 mm | 39 mil |
| Water vapour transmission (Sd) | EN 1931 | 0,1 m | 34.965 US perm |
| Tensile strength MD/CD | EN 12311-1 | 380 / 420 N/50mm | 43 / 48 lbf/in |
| Elongation MD/CD | EN 12311-1 | 40 / 55 % | - |
| Resistance to nail tearing MD/CD | EN 12310-1 | 220 / 210 N | 49 / 47 lbf |
| Watertightness | EN 1928 | class W1 | - |
| Resistance to temperature | - | -40 / 120 °C | -40 / 248 °F |
| Reaction to fire | EN 13501-1 | class B-s1,d2 | - |
| Resistance to penetration of air | EN 12114 | < 0,02 m³/(m²·h·50Pa) | < 0.001 cfm/ft² at 50Pa |
| Thermal conductivity (λ) | - | 0,2 W/(m·K) | 0.12 BTU/(h·ft·°F) |
| Specific heat | - | 1300 J/(kg·K) | - |
| Density | - | ca. 210 kg/m³ | - |
| Water vapour resistance factor (μ) | - | ca. 100 | - |
| UV resistance without final coating | EN 13859-2 | 5000h (>12 mesi) | - |
| UV stability with joints up to 30 mm wide exposing no more than 30% of the surface (1 ) | EN 13859-2 | permanent | - |
| Water column | ISO 811 | > 300 cm | > 118 in |
| Watertightness after artificial ageing | EN 1297 / EN 1928 | class W1 | - |
| After artificial ageing - Tensile strength MD/CD | EN 1297 / EN 12311-1 | 340 / 380 N/50mm | 39 / 43 lb/in |
| After artificial ageing - elongation | EN 1297 / EN 12311-1 | 35 / 50 % | - |
| Flexibility at low temperatures | EN 1109 | -30 °C | -22 °F |
| VOC | - | not relevant | - |
1. The membrane is not intended as a final waterproof layer for roofs.
Composition
| TOP LAYER | breathable monolithic PU film |
|---|---|
| REINFORCING LAYER | PL fabric |
Specifications
TRASPIR FELT EVO UV 210
Supply and installation of UV-resistant monolithic breathable membrane, Type TRASPIR FELT EVO UV 210.
Composition
From top layer to bottom layer:
breathable monolithic PU film;
PL fabric
Properties
Mass per unit area [g/m²]: 210
Thickness [mm]: 1
Water vapour transmission (Sd)[m]: 0,1
Tensile strength MD/CD [N/50 mm]: 380/420
Elongation MD/CD [%]: 40/55
Resistance to nail tearing MD/CD [N]: 220/210
Watertightness: class W1 (EN 1928)
Reaction to fire: class B-s1, d2 (EN 13501-1)
Resistance to temperature [C°]: -40/120
UV resistance without final coating: 5000h (>12 months)
VOC [%]: not applicable
Standards and certifications
CE marked in accordance with EN 13859-1/2
AUS 4200.1 Class 4
Description
The application surface must be dry, free of dust and grease. Surface elements must be removed so that the membrane is not damaged during application.
Recommended use: direct UV protection is guaranteed. Installation is therefore permitted on both the internal and external sides of the building envelope.
Installation: Unroll the membrane and seal using tape such as: DOUBLE BAND, FACADE BAND or FRONT BAND UV.
Installation in compliance with the B-s1, d2 value: Unroll the membrane and seal using tape such as: MULTI BAND UV or type FRONT BAND UV 210.
Ensure that the overlap between the membranes is at least 15 cm to achieve an optimal seal.
To ensure correct and professional installation, the use of a nail sealing point is required.
Further details regarding installation can be found in the specific instructions provided by the supplier.